摘要
本文以氟硅酸铵和碳酸氢铵为原料制备白炭黑和氟化铵(NH_(4)F)。根据单因素实验并结合Box-Behnken响应面法建立二次回归模型进行方差分析和验证,考察了液固比、配料比、反应温度、反应时间四个因素对白炭黑收率和NH_(4)F浓度的影响,通过响应面法优化得到较优工艺条件:液固比8,配料比5.49,反应温度76.5℃,反应时间49.08 min。在该工艺条件下进行验证实验得到白炭黑收率为96.90%,NH_(4)F浓度为2.02 mol/L,预测值与实验值无显著差异,验证了二次回归模型的可靠性。对产品白炭黑进行XRD、IR、TG-DSC、SEM、BET表征,及粒度分析和性能测试,对于产品NH_(4)F,采用氟离子选择性电极法测定其浓度,并对其性能进行检测。证实了白炭黑产品粒度为微米级,且是一种比表面积达316.83 m^(2)/g的介孔材料,其中SiO_(2)的质量分数高达97.77%,外观、加热减量、灼烧减量、pH值、重金属含量和吸油值均达到行业标准。NH_(4)F产品中氟化铵含量、游离酸含量和氟硅酸盐含量均达到国家标准。
Ammonium hexafluorosilicate and ammonium bicarbonate as raw materials were used to prepare silica and ammonium fluoride(NH_(4)F).Based on the single factor experiment and Box-Behnken design response surface methodology,a quadratic regression model was established for variance analysis and verification.The influences of four single factors(liquid-solid ratio,ingredient ratio,reaction temperature and reaction time) on silica yield and NH_(4)F concentration were investigated.By the response surface analysis,the better process conditions are as follows:liquid-solid ratio 8,ingredient ratio 5.49,reaction temperature 76.5 ℃,reaction time 49.08 min.Under these conditions,the verification experiment was carried out.The silica yield is 96.90%,and the NH_(4)F concentration is 2.02 mol/L.There is no significant difference between the predicted value and the experimental value,which verifies the reliability of the quadratic regression model.XRD,IR,TG-DSC,SEM,BET characterization,particle size analysis and performance test of the product silica were carried out.The concentration of the product NH_(4)F was measured by the fluoride ion selective electrode method,and its performance was tested.It is confirmed that the particle size of silica product is micron-sized,and silica is a mesoporous material with specific surface area of 316.83 m^(2)/g.The mass fraction of SiO_(2)is as high as 97.77%,and the appearance,heating loss,ignition loss,pH value,heavy metal content,and oil absorption value all meet industry standards.The content of ammonium fluoride,free acid and fluorosilicate in NH_(4)F product all meets the national standard of the People’s Republic of China.
作者
马腾
王泽琦
任一鸣
朱留凯
李涛
任保增
MA Teng;WANG Zeqi;REN Yiming;ZHU Liukai;LI Tao;REN Baozeng(School of Chemical Engineering,Zhengzhou University,Zhengzhou 450001,China)
出处
《硅酸盐通报》
CAS
北大核心
2022年第3期940-952,975,共14页
Bulletin of the Chinese Ceramic Society
基金
国家重点研发计划(2017YFC0212404)
河南省高等学校重点科研项目(19A530004)。
关键词
电子废弃物
氟硅酸铵
白炭黑
氟化铵
响应面法
工艺优化
electronic waste
ammonium hexafluorosilicate
silica
ammonium fluoride
response surface methodology
process optimization