This work aims at solving the problems of difficult dispersion,easy oxidation and high cost of nano carbon during application,carbon/magnesium aluminate spinel(C/MgAl_(2)O_(4))composite powders were prepared using MgC2O4·2H2O,MgO2,Al2O3 powder,and Al powder as raw materials by combustion synthesis.The results indicate that with the maximum MgC2O4·2H2O addition of 33.34 mass%,the prepared powder contains 1.17 mass%of carbon and carbon distributes among spinel grains.The MgAl_(2)O_(4)spinel shows both granular and rod-like morphologies.The granular MgAl_(2)O_(4)spinel is generated from mutual diffusion between MgO and Al2O3;while the rod-like MgAl_(2)O_(4)spinel is mainly formed by the vapor-solid growth mechanism from Mg vapor and Al2O3.