摘要
在低温下用氢氧化钠/尿素混合液提取大蒜皮里的纤维素,再加入质量分数为0.05的高锰酸钾(KMnO_(4))溶液析出纳米纤维素,并采用傅里叶红外光谱、扫描电子显微镜和X射线衍射谱对其进行表征,结果表明该法提取的纳米纤维素的结晶度较高,达到73.8%。结合纳米纤维素的热重分析可以推测,KMnO_(4)溶液处理所得的纳米纤维素具有较好的力学性能。
The cellulose in garlic skin was extracted by sodium hydroxide(NaOH)/urea mixture at low temperature,and then nano cellulose was precipitated by adding potassium permanganate(KMnO_(4))solution with a mass fraction of 0.05.The nano cellulose was characterized by Fourier transform infrared spectroscopy,scanning electron microscopy and X-ray diffraction spectroscopy.The results showed that the crystallinity of nano cellulose extracted by this method was relatively high,reaching 73.8%.Combined with the thermogravimetric analysis of nano cellulose,it could be inferred that the nano cellulose treated with KMnO_(4) solution had excellent mechanical properties.
作者
汪传生
刘庄宇
边慧光
WANG Chuansheng;LIU Zhuangyu;BIAN Huiguang(Qingdao University of Science and Technology,Qingdao 266061,China)
出处
《橡胶工业》
CAS
2021年第9期670-675,共6页
China Rubber Industry
基金
山东省重点研发计划项目(2019GGX102018)
山东省自然科学基金资助项目(ZR2016XJ003)
青创科技计划项目(2019KJB007)。
关键词
纳米纤维素
大蒜皮
结晶度
低温提取
氢氧化钠
尿素
高锰酸钾
析出
nano cellulose
garlic skin
crystallinity
low temperature extraction
NaOH
urea
KMnO4
precipitation
作者简介
汪传生(1960-),男,安徽潜山人,青岛科技大学教授,博士,主要从事高分子材料先进制造技术和废旧橡胶塑料循环利用的研究工作;通信联系人:边慧光,(bianhuiguang@163.com)。