摘要
In this study,the Heishan coal was used to prepare a series of activated carbon(AC)samples via a vapor deposition method.The effects of the Fe(NO_(3))3/coal weight ratio on the physicochemical properties of the activated carbon were systematically investigated,and the AC samples were analyzed by the N2 adsorption-desorption technique,the scanning electron microscopy,the X-ray diffraction,the Raman spectroscopy,and the Fourier transform infrared spectroscopy.Furthermore,the adsorption properties of ethyl acetate were investigated.The results indicated that as the Fe(NO_(3))3/coal mass ratio increased from 1:8 to 1:2,the specific surface area,the total pore volume and the micropore volume initially increased and then decreased.The specific surface area increased from 560.86 m^(2)/g to 685.90 m^(2)/g,and then decreased to 299.56 m^(2)/g.The total pore volume and micropore volume increased from 0.29 cm^(3)/g and 0.17 cm^(3)/g to 0.30 cm^(3)/g and 0.22 cm^(3)/g,and then decreased to 0.16 cm^(3)/g and 0.10 cm^(3)/g,respectively.The optimized ratio was 1:8.During the activation process,iron ions infiltrated the activated carbon to promote the development of the pore structure,the pore size of which was between 2.5 nm and 3 nm in daimeter.This approach could enhance the capacity for adsorption of ethyl acetate.It is worth noting that the ACs displaying the largest specific surface area and total pore volume(685.90 m^(2)/g and 0.30 cm^(3)/g)were formed under the optimized activation conditions(950℃,20%(volume)of CO_(2),ratio 1:5),and the maximum AC capacity for adsorption of ethyl acetate was 962.62 mg/g.After seven repeated thermal regeneration experiments,the saturated AC adsorption capacity was still above 90%.
基金
The authors thank the National Natural Science Foundation of China(No.51906130)
the Natural Science Foundation of Shandong Province(No.ZR2019BEE053)
the Key R&D and Development Plan of Shandong Province(2020CXGC011401)
the Foundation of Shandong Key Lab of Energy Carbon Reduction and Resource Utilization,Shandong University(No.ECRRU201804)for the financial support.
作者简介
Corresponding Author:Professor Wang Luyuan,E-mail:luyuanwang1988@126.com.