摘要
以有机硅为成膜物,复配高效隔热填料和增强填料等,制备了一种可以耐受500℃、1 h,且不发生起泡、开裂、脱落可反复使用的耐高温隔热有机涂料。对涂层的耐热性和隔热性能进行了测试,采用马弗炉对厚度为4 mm的涂层加热500℃、1 h后,发现涂层不开裂、不起泡、不脱落,该涂层具备良好的耐热性。复配高效隔热填料质量分数为80%时,涂层的导热系数低于0.08 W(/m·K),具有良好的隔热性能。并且,对涂层的耐高温隔热的原理进行了分析,发现耐热填料、助溶剂和隔热填料等有效复配是涂层耐热隔热的关键。该涂料具备良好的应用前景,可应用于高温管道等的隔热保温。
Reusable high-temperature heat-insulating silicone coatings capable of withstanding the temperature of 500℃for an hour without blistering,cracking or peeling were prepared with silicone as the main film forming material,effective heat-insulating fillers,reinforcing fillers,etc.The heat resistance and heat-insulating performance of coatings were tested.The silicone coatings 4 mm thick were heated at 500℃in a muffle furnace for an hour without cracking,blistering or shedding,demonstrating the coatings had excellent heat resistance.The thermal conductivity coefficient of the coatings was below 0.08 W/(m·K),when the weight ratio of thermal insulation fillers is 80%,indicating the coatings had good heat-insulating performance.An analysis of the coatings’high temperature resistance and heat insulation principles shows that effective combination of heat-resistant fillers,cosolvents and thermal insulation fillers is the key to the heat resistance of the coatings.The coatings have good application prospects and can be applied for heat insulation of high-temperature pipelines,etc.
作者
吴连锋
王飞
王贤明
宁亮
易敏华
刘雷雷
卢敏
WU Lian-feng;WANG Fei;WANG Xian-ming;NING Liang;YI Min-hua;LIU Lei-lei;LU Min(State Key Laboratory of Marine Coatings,Marine Chemical Research Institute Co.,Ltd.,Qingdao 266071,Shandong,China)
出处
《中国涂料》
CAS
2021年第6期14-18,共5页
China Coatings
基金
在航科学基金(薄层轻质防热涂层在湿热紫外环境下的性能演化机理研究)(20180112008)。
关键词
有机硅涂料
长时耐热性
隔热性
silicone coatings
long-time heat resistance
thermal insulation
作者简介
吴连锋(1986-),男(汉族),山东泰安人。高级工程师,硕士,主要从事耐高温涂料、抗静电涂料、隔热涂料、透波涂料等功能涂料的研究。