以碱法降解废弃皮革革屑提取的胶原降解物为原料,环氧氯丙烷为交联剂制备木材蛋白胶。通过控制环氧氯丙烷的用量,反应温度,反应时间以及pH的正交法合成蛋白胶(CA)。以CA胶的黏度、胶合板的胶合强度评估优化合成条件。根据优化条件合成的CA胶黏剂的含固量约42.0%,黏度为1.56 Pa·s。胶合板的主要质量指标满足GB/T9846-2015中Ⅰ、Ⅱ型要求。
The wood protein glue is prepared by using the collagen degradation product extracted from the waste leather shavings by the alkaline method as the raw material and epichlorohydrin as the cross-linking agent. By controlling the amount of epichlorohydrin, reaction temperature, reaction time and pH orthogonal method to synthesize protein glue(CA).Optimize the synthesis conditions by evaluating the viscosity of CA glue and the bonding strength of plywood. The CA adhesive synthesized under the optimized conditions has a solid content of about 42.0% and a viscosity of 1.56 Pa·s. The main quality indicators of plywood meet the requirements of Type Ⅰ and Type Ⅱ in GB/T9846-2015.
作者
蒲红霞
纪丁愈
张一炜
戴睿
陈慧
单志华
PU Hongxia;JI Dingyu;ZHANG Yiwei;DAI Rui;CHEN Hui;SHAN Zhihua(College of BiomassScience and Engineering,Sichuan University,Chengdu 610065,China;National Engineering Research Center of Clean Technology in Leather Industry,Sichuan University,Chengdu 610065,China;Department of Resource and Environment Engineering,Sichuan Water Conservancy Vocational College,Chengdu 61231,China)
出处
《皮革科学与工程》
CAS
北大核心
2021年第3期36-40,45,共6页
Leather Science and Engineering
基金
蛋白胶粘剂对胶合板无醛催化粘接机制与应用研究(2019YFG0269)
四川循环经济研究中心课题资助(XHJJ-2009)。
关键词
废弃革屑
胶合板
蛋白胶黏剂
力学性能
waste leather shavings
plywood
protein adhesive
mechanical properties