摘要
以漂白针叶木浆为原料,氯乙酸钠为醚化剂,在碱醇体系下制备羧甲基改性纤维素。以纤维的羧基含量为评价指标,探究出较佳工艺条件为:纤维素与氢氧化钠、氯乙酸钠的质量比为1:0.30∶1.05-1.20,反应温度为70℃-75℃,反应时间为50-60 min。通过光学显微镜观察羧甲基改性前后纤维微观形态尤其是润胀情况的变化。羧甲基改性前后的纤维X-射线衍射分析,证明了改性后纤维的晶型结构没有发生变化,仍然为纤维素I型。制备出的羧甲基改性纤维素浆采用抄纸法可快速制备成高强纤维素膜。纤维素膜初始热降解温度为290.4℃,在700℃的残余物含量约为39%;可见光区的光透过率最高可达90%左右;拉伸强度和耐破指数随羧基含量的增加而增大,最高可达到148.2 Mpa、12.59 Kpa·m^(2)·g^(-1),但撕裂指数随着羧基含量的增加而下降。
Using bleached softwood pulp and sodium chloroacetate to prepare carboxymethyl modified cellulose in an alkali-alcohol system.The best process condition:the mass ratio of cellulose to sodium hydroxide and sodium chloroacetate was 1∶0.30∶1.05-1.20,temperature was 70℃-75℃and the reaction time was 60-70 min.Carboxymethyl-modified cellulose could be quickly prepared into high-strength cellulose film through papermaking method.The initial thermal degradation temperature of the film is 290.4℃,the residue content at 700℃is 39%.The light transmittance can reach about 90%.The tensile strength and bursting index of the cellulose film increased with the carboxyl group content,up to 148.2 Mpa and 12.59 Kpa·m2·g-1.But the tearing index showed a continuous downward trend.
作者
李方
雷春发
陈港
LI Fang;LEI Chunfa;CHEN Gang(State Key Lab of Pulp&Paper Engineering,South China University of Technology,Guangzhou 510640,China)
出处
《造纸科学与技术》
2021年第1期23-28,44,共7页
Paper Science & Technology
基金
国家重点研发计划项目(2018YFC1902102)
华南理工大学制浆造纸工程国家重点实验室自主创新研究基金(2020ZD02)。
关键词
氯乙酸钠
羧甲基改性纤维素
抄纸法
羧基含量
sodium chloroacetate
carboxymethyl modified cellulose
papermaking method
carboxyl content