摘要
综述了典型钢材在常规高温加工成型、燃煤、垃圾焚烧和火灾4种环境下气氛对其热蚀行为和腐蚀机理影响的相关研究,特别是气氛对典型钢材氧化产物形态和相组成的影响。目前研究的方向主要集中在评价钢板耐腐蚀性能、确定影响耐腐蚀性能的关键因素等方面。
The related research development of influence of atmosphere in common high temperature processing, coal burning, waste incinerating and fire on the hot corrosion behavior and corrosion mechanism of typical steel,were summarized,especially, the influence of atmosphere on the morphology and phase composition of corrosion product of typical steel. The research direction mainly focus on the evaluation of corrosion resistance of steel and the determination of the key factors affecting the corrosion resistance.
作者
杨振鑫
栾林硕
张晟源
金静
邓亮
YANG Zhenxin;LUAN Linshuo;ZHANG Shengyuan;JIN Jing;DENG Liang(College of Investigation,China People's Police University,Langfang 065000,China;Graduate Department,China People's Police University,Langfang 065000,China)
出处
《热加工工艺》
北大核心
2021年第2期1-5,9,共6页
Hot Working Technology
基金
河北省重点研发计划项目(18215416)。
关键词
钢材
高温热蚀
氧气
水蒸气
腐蚀性气氛
燃煤环境
垃圾焚烧
steel
high-temperature hot corrosion
oxygen
vapor
corrosive atmosphere
coal environment
waste incineration
作者简介
杨振鑫(1997-),男,上海人,主要研究方向为火灾调查,电话:15395432839,E-mail:y.yzx@foxmail.com;通讯作者:金静(1986-),女,安徽宿州人,副教授,博士,主要从事火场痕迹识别、火灾原因认定方面的研究,电话:15369659708,E-mail:jinj@iccas.ac.cn。