摘要
为合成一种新型氮磷阻燃剂,以1,3—二[三(羟甲基)甲氨基]丙烷、三氯氧磷为主要原料,将合成的新型磷氮阻燃剂应用于大麻织物上。通过红外光谱FT-IR、热稳定性分析TG、损毁炭长等方法对制备的阻燃剂和阻燃效果进行结构表征和分析。研究结果表明:当n(1,3—二[三(羟甲基)甲氨基]丙烷):n(三氯氧磷)=1∶3,反应时间为5 h,反应温度为75℃,三乙胺用量为3 g/L时,制备的阻燃剂稳定性好,对大麻织物的阻燃效果最佳。
In order to synthesize a new type of nitrogen-phosphorus flame retardant,using 1,3-bis[tris(hydroxymethyl)methylamino]propane and phosphorus oxychloride as the main raw materials,the synthesized new type of phosphorus-nitrogen flame retardant was applied to hemp fabrics on.The structure characterization and the effect of the prepared flame retardant were analyzed by FT-IR,TG,damaged carbon length,etc.The results show that when n(1,3-bis[tris(hydroxymethyl)methylamino]propane)∶n(phosphoric oxychloride)=1∶3,the reaction time is 5 h;reaction temperature is 75℃,the triethylamine dosage is 3g/L,the prepared flame retardant has good stability and the best flame retardant effect on hemp fabric.
作者
王迪
赵欣
夏宁
WANG Di;ZHAO Xin;XIA Ning(College of Light Industry and Textile,Qiqihar University,Qiqihar,Heilongjiang 161000,China;Linen Process Engineering Technology Research and Development Centre,Qiqihar University,Qiqihar,Heilongjiang 161000,China)
出处
《毛纺科技》
CAS
北大核心
2020年第12期28-31,共4页
Wool Textile Journal
基金
黑龙江省教育厅基本业务专项(135209208)。
关键词
氮磷阻燃剂
1
3—二[三(羟甲基)甲氨基]丙烷
三氯氧磷
大麻织物
nitrogen phosphorus flame retardant
1,3-bis[tris(hydroxymethyl)methylamino]propane
phosphorus oxychloride
hemp fabric
作者简介
第一作者:王迪,硕士生,主要研究方向为麻类织物的阻燃整理;通信作者:赵欣,教授,主要研究方向为阻燃剂的合成与应用,E-mail:zx427213@sina.com。