Aqueous zinc-ion batteries have been regarded as a promising alternative to large-scale energy storage, due to associated low-cost, improved safety and environmental friendliness. However, a high-performance cathode material for both rate capability and specific capacity is still a challenge. One kind of the more promising candidates are sodium manganese oxide(NMO) materials, although they suffer from individual issues and need to be further improved. Herein, we present a novel mixed phase NMO material composed of nearly equal amounts of Na(0.55)Mn2O4 and Na(0.7)MnO(2.05). The structured configuration with particle size of 200–500 nm is found to be beneficial towards improving the ion diffusion rate during the charge/discharge process. Compared with Na(0.7)MnO(2.05) and Na(0.55)Mn2O4, the mixed phase NMO demonstrates an enhanced rate capability and excellent long-term cycling stability with a capacity retention of 83% after 800 cycles. More importantly, the system also delivers an impressive energy density and power density, as 378 W·h·kg^-1 at 68.7 W·kg^-1, or 172 W·h·kg^-1 at 1705 W·kg^-1. The superior electrochemical performance is ascribed to the fast Zn^2+ diffusion rate because of a large ratio of capacitive contribution(63.9% at 0.9 m V·s^-1). Thus, the mixed phase route provides a novel strategy to enhance electrochemical performance, enabling mixed phase NMO as very promising material towards large-scale energy-storage applications.
基金
the financial support from the China Scholarship Council(CSC)
supported by the National Natural Science Foundation of China(21905037)
the Fundamental Research Funds for the Central Universities(3132019328,3132020151)。
作者简介
Corresponding authors:Xinyu Wang.E-mail addresses:wangxinyu@dlmu.edu.cn;Corresponding authors:Qiongqiong Lu.E-mail addressesq.lu@ifw-dresden.de.