A new Cu-based bulk metallic glass composite of nominal composition(at.%)Cu41Ni27Ti25Al7 with excellent plasticity and a strong work-hardening behavior is fabricated.Strength above 1859 MPa and plasticity more than 11%are achieved under compression and tension modes.The deformation mechanism is proposed to the structural heterogeneities of the composite that promotes multiple shear bands meanwhile inhibits their free propagation,which results in the macroscopically plastic strain and work hardening.The alloy contains relatively cheap metals and has a low cost,which is beneficial to industrial applications.
作者
Dong-Mei Li
Lan-Sheng Chen
Peng Yu
Ding Ding
Lei Xia
李冬梅;陈澜生;余鹏;丁鼎;夏雷(Chongqing Key Laboratory of Photo-Electric Functional Materials,College of Physics and Electronic Engineering,Chongqing Normal University,Chongqing 401331,China;Laboratory for Microstructure&Institute of Materials,Shanghai University,Shanghai 200072,China)
基金
Supported by the Chongqing Research Program of Basic Research and Frontier Technology(Grant Nos.cstc2018jcyjAX0329 and cstc2018jcyjAX0444)
the Science and Technology Research Program of Chongqing Municipal Education Commission(Grant No.KJZD-K201900501).
作者简介
Corresponding author:余鹏,Email:pengyu@cqnu.edu.cn。