摘要
以磷石膏和炭化污泥为主要原料,氢氧化钠为激发剂,采用一步法制备磷石膏-炭化污泥胶凝材料,通过对炭化污泥/磷石膏配比、水泥掺量对力学性能影响的试验研究,确定磷石膏-炭化污泥胶凝材料配比。结果表明:在标准养护条件下,随着水泥掺量降低,磷石膏-炭化污泥胶凝材料强度亦降低。当炭化污泥/磷石膏=6:4时,早期抗折强度最高可达4.2 MPa,抗压强度为15.2 MPa。
Using carbonized sludge and phosphogypsum as main raw materials,sodium hydroxide as excitation agent,carbonized sludge/phosphogypsum-based cementing composite was developed.Mix ratio of the carbonized sludge/phosphogypsum-based cementing composite was determined by lots of tests on the proportional ratio of carbonized sludge,phosphogypsum and cement.The results showed that under standard curing condition,the early compressive strength of the carbonized sludge/phosphogypsum-based cementing composite prepared with the mix ratio of carbonized sludge/phosphogypsum=6:4 could reach 15.2 Mpa,and the flexural strength is up to 4.2 MPa.
作者
胡敏
彭丽
郭娜
颜子博
Hu Min;Peng Li;Guo Na;Yan Zibo(Deyang Research Center of Building Materials and Environmental Resource Engineering Technology,Deyang,Sichuan,China;College of materials and chemistry&chemical engineering,Chengdu university of technology,Chengdu,Sichuan,China)
出处
《矿产综合利用》
CAS
北大核心
2020年第4期196-201,共6页
Multipurpose Utilization of Mineral Resources
基金
德阳市科技局应用技术研究与开发资金项目(2015ZZ037)
温州市基础性科研项目(G20180033)。
关键词
激发剂
工业废渣
资源化
复合胶凝材料
力学性能
The excitation agent
Industrial waste
Utilization of waste
Cementing composite
Mechanical property