采用激光熔化沉积和铸造技术分别制备了CrMnFeCoNi高熵合金。通过X射线衍射(XRD)、金相腐蚀、扫描电镜(SEM)和力学拉伸实验等分析手段对不同方法制备的CrMnFeCoNi高熵合金相组成、微观组织及力学性能进行了对比研究。结果表明:通过激光熔化沉积和铸造技术制备的CrMnFeCoNi高熵合金均为面心立方(FCC)单相固溶体结构;采用激光熔化沉积技术制备的CrMnFeCoNi高熵合金具有更为均匀的元素分布;随着温度从293 K降低到77 K,激光熔化沉积技术制备的CrMnFeCoNi高熵合金的拉伸强度与塑性分别从518 MPa、55%提升到878 MPa、95%,表现出优异的低温力学性能。
CrMnFeCoNi high-entropy alloys were prepared by laser melting deposition(LMD)and casting,respectively.The phase composition,microstructure and mechanical properties of the CrMnFeCoNi high-entropy alloys were studied by means of X-ray diffraction(XRD),metallographic corrosion,scanning electron microscopy(SEM)and mechanical tensile test.The results show that the CrMnFeCoNi high entropy alloys prepared by laser melting deposition and casting technology are face centered cubic(FCC)single phase solid solution structure,and the CrMnFeCoNi high entropy alloys prepared by laser melting deposition have more uniform element distribution.With the decrease of temperature from 293 K to 77 K,the tensile strength and plasticity of the CrMnFeCoNi high entropy alloys prepared by laser melting deposition increase from 518 MPa and 55%to 878 MPa and 95%,respectively,showing excellent mechanical properties at low temperature.
作者
阿卜杜喀迪尔·艾麦尔
向硕
乐国敏
刘学
李强
李晋锋
ABDUKADIR A-mar;XIANG Shuo;LE Guo-min;LIU Xue;LI Qiang;LI Jin-feng(Institute of Materials,China Academy of Engineering Physics,Jiangyou 621908,China;College of Physics and Technology,Xinjiang University,Urumqi 830046,China)
出处
《材料热处理学报》
EI
CAS
CSCD
北大核心
2020年第3期70-75,共6页
Transactions of Materials and Heat Treatment
基金
四川省科技计划项目(2018G20146)
攀枝花财政科技专项资金项目(2017CY-G-21)。
关键词
高熵合金
激光熔化沉积
低温
拉伸断口
high-entropy alloy
laser melting deposition
low temperature
fracture surface
作者简介
阿卜杜喀迪尔·艾麦尔(1992-),男,硕士,主要从事高熵合金研究,E-mail:abdukadiramar@163.com;通信作者:李晋锋(1986-),男,博士,主要从事非晶与高熵合金研究,已发表论文30篇,E-mail:lijinfeng305@126.com。