基于特定铁精粉配比,通过改变w(MgO),对镁质酸性球团制备及其冶金性能进行了详细实验研究。结果表明:当w(SiO2)为5.5%,w(MgO)在1.4%~2.2%之间变化时,w(MgO)对铁矿粉的成球率、生球强度影响不大;球团爆裂温度呈先降低后升高的趋势,且在w(MgO)为2.0%时,爆裂温度最低;抗压强度呈下降的趋势,w(MgO)每增加0.1%,抗压强度降低71.9 N/P;低温还原粉化性呈先降低后升高的趋势,w(MgO)每增加0.1%,还原性能降低1.6%,总体软化性能得到改善。
Based on the specific iron concentrate ratio,detailed experimental studies on the preparation and metallurgical properties of magnesium acidic pellets are made by changing w(MgO).The results show that when w(SiO2) is 5.5% and w(MgO) varies from 1.4% to 2.2%,w(MgO) has little effect on the spheronization rate and green pellet strength of iron ore powder;the burst temperature of pellets decreases first and then increases,and is at the lowest when w(MgO) is 2.0%;the compressive strength shows a downward trend,with each increase of w(MgO) by 0.1%,the compressive strength decreases by 71.9 N/P;the tendency of low-temperature reduction and pulverization decreases first and then increases,with each increase of w(MgO) by 0.1%,reduction performance decreases by 1.6%,the overall softening performance is improved.
作者
王晓磊
师学峰
胡长庆
韩伟刚
赵凯
Wang Xiaolei;Shi Xuefeng;Hu Changqing;Han Weigang;Zhao Kai(School of Metallurgy and Energy,North China University of Science and Technology,Tangshan 063210,Hebei)
出处
《烧结球团》
北大核心
2020年第1期35-39,共5页
Sintering and Pelletizing
基金
国家重点研发计划资助项目(2017YFC0210600)。
关键词
MGO
酸性球团
成球率
爆裂温度
冶金性能
MgO
acidic pellets
spheronization rate
burst temperature
metallurgical properties
作者简介
王晓磊(1992-),男,硕士研究生,从事炼铁原料工艺方面的研究;通讯作者:胡长庆(1973-),男,博士,教授,从事铁矿粉造块、炼铁和钢铁工业能源环境的相关研究。