摘要
本文研究了溶剂型聚氨酯在合成革中的展色性能,以4,4-二苯基甲烷二苯基甲烷二异氰酸酯、己二酸、乙二醇、1,4-丁二醇、甲基丙二醇、N,N-二甲基甲酰胺及乙酸乙酯为主要原料。考察了多元醇组成、扩链剂种类及溶剂组成等因素对干法聚氨酯合成革展色性影响规律。结果表明,当己二酸系聚酯二元醇中乙二醇与1,4-丁二醇的摩尔比为1∶1时、所用扩链剂组成为乙二醇与甲基丙二醇的摩尔比为1∶0.5,所使用的溶剂中N,N-二甲基甲酰胺与乙酸乙酯的质量比为2∶1时,制备得到的干法聚氨酯合成革的展色性能最佳(偏蓝相)。
This paper studied the color development properties of solvent-based polyurethanes in synthetic leather,with 4,4-diphenylmethanediphenylmethane diisocyanate,adipic acid,ethylene glycol,1,4-butanediol,and AA.Propylene glycol,N,N-dimethylformamide and ethyl acetate are the main raw materials.The effects of polyol composition,chain extender type and solvent composition on the color development of dry polyurethane synthetic leather were investigated.The results show that when the molar ratio of ethylene glycol to 1,4-butanediol in the adipic acid polyester diol is 1∶1,the chain extender composition is the molar ratio of ethylene glycol to methyl propylene glycol.When the mass ratio of N,N-dimethylformamide to ethyl acetate in the solvent used is 1∶0.5,the prepared dry polyurethane synthetic leather has the best color development performance(blue phase).
作者
诸昌武
潘顾源
王元有
金党琴
徐嘉琪
ZHU chang-wu;PAN gu-yuan;WANG yuan-you;JIN dang-qin;XU jia-qi(Department of Chemical Engineering,Yangzhou Polytechnic Institute,Yangzhou,225127 China)
出处
《化学研究与应用》
CAS
CSCD
北大核心
2020年第1期139-142,共4页
Chemical Research and Application
基金
2017年江苏省高等学校优秀科技创新团队项目(苏教科[2017]6号)资助
扬州市市校合作专项项目(YZ2018148资助
扬州市自然科学基金项目(YZ2018099))资助
江苏省高等学校大学生创新创业训练计划(201914635018X)资助
扬州工业职业技术学院自然科技类2019年重点课题“无溶剂多羟基水性丙烯酸分散体的关键技术研究”资助
关键词
溶剂型聚氨酯
干法聚氨酯合成革
展色性能
solvent-based polyurethane
dry polyurethane synthetic leather
color development performance
作者简介
联系人:王元有(1977-),男,博士,副教授,主要研究方向为纳米材料及性能研究。E-mail:wangyy@ypi.edu.cn。