利用甘氨酸-硝酸盐燃烧法制备不同浓度Co掺杂的La0.8Sr0.2Ga0.8-xMg0.2CoxO3-δ固体氧化物燃料电池电解质材料,并对其晶体结构、形貌以及电学性能进行表征.结果表明:随着Co掺杂量的增加,样品无明显杂相峰,其谱峰略向小角度一侧移动,晶胞体积略增大,平均粒径逐渐减小;Co掺杂对电导率影响显著,晶粒电导率是导致样品总电导率升高的主要因素.
The La 0.8 Sr 0.2 Ga 0.8-x Mg 0.2 Co x O 3-δelectrolytes for solid oxide fuel cell(SOFC)with different concentrations of Co were prepared by glycine-nitrate combustion method,and the crystal st ructure,morphology and electrical properties were characterized.The results sh ow that,with the increase of Co doping,there is no obvious heter ophase peak in the sample,the spectral peaks shift slightly to the side of smal l angle,the cell volume increases slightly,and the average partical size decre ases gradually.Co doping has a siginificant effect on the conductivity,and t he grain conductivity is the key factor to increase the total conductivity of the sample.
作者
张国栋
王欢
王利行
常笑鹏
宋浩冉
骆泽阳
徐培
王德军
ZHANG Guodong;WANG Huan;WANG Lihang;CHANG Xiaopeng;SONG Haoran;LUO Zeyang;XU Pei;WANG Dejun(Key Laboratory of Materials Design and Quantum Simulation,Col lege of Science,Changchun University,Changchun 130022,China;Graduate College,Changchun University,Changchun 130022,China)
出处
《吉林大学学报（理学版）》
CAS
北大核心
2020年第1期162-165,共4页
Journal of Jilin University:Science Edition
基金
吉林省自然科学基金（批准号：20190201105JC）
吉林省发改委高技术产业创新项目（批准号：2018C043-1）
吉林省教育厅“十三五”科学技术研究项目（批准号：JJKH2018018KJ）
作者简介
第一作者简介:张国栋(1994-),男,汉族,硕士研究生,从事燃料电池的研究,E-mail:819965473@qq.com;通信作者:王德军(1971-),男,汉族,博士,教授,从事新能源材料的研究,E-mail:272951353@qq.com.