摘要
通过静电纺丝技术和高温碳化制备了石墨烯/镧共掺杂TiO2纳米纤维。采用扫描电子显微镜、X-射线衍射仪、红外光谱仪及紫外分光光度计对纳米纤维的形貌、结构和光催化性能进行了表征和测试。结果表明,石墨烯的掺杂可以提高TiO2纳米纤维的光催化性能,当石墨烯掺杂量为0.1 g时,TiO2纳米纤维的光催化性能较优。
Graphene/La3+co-doped TiO2 nanofibers are prepared by electrospinning technique and high temperature carbonization.Themorphology,structure and photocatalytic properties nanofibers are characterized and tested by scanning electron microscope,X-raydiffractometer,infrared spectrometer and ultraviolet spectrophotometer.The results show that the doping of graphene could improve thephotocatalytic properties of TiO2 nanofibers.when the doping content of graphene is 0.1 g,the photocatalytic performance of TiO2 nanofibersis the best.
作者
吴金垚
王芳芳
徐思峻
周蓉
徐山青
WU Jinyao;WANG Fangfang;XU Sijun;ZHOU Rong;XU Shanqing(School of Textile and Clothing,Nantong University,Nantong 226019,China)
出处
《上海纺织科技》
北大核心
2019年第12期74-77,共4页
Shanghai Textile Science & Technology
基金
国家自然科学基金青年基金项目(51703098、51403106)
关键词
石墨烯
镧
静电纺丝
纳米纤维
光催化性能
graphene
La3+
electrospinning
nanofibers
photocatalytic performance
作者简介
吴金垚(1993-),男,硕士,主要从事光催化材料的研究;通信作者:徐山青。E-mail:xu.sq@ntu.edu.cn。