65Mn弹簧钢丝生产的拉簧服役几个月后发生断裂。采用SEM扫描电子显微镜对弹簧断口表面进行形貌、金相组织等检测,对弹簧断裂原因及断裂过程进行分析。结果表明,弹簧断口为疲劳失效断口,疲劳源处表面微裂纹是引起疲劳裂纹萌生的直接原因,表面微裂纹则是由不良抛丸工艺造成的。弹簧厂通过更换新钢丸并降低抛丸速度消除了疲劳性能不符合要求的情况。
The pull spring of 65Mn spring steel wire broke after several months’service.The SEM was used to detect the surface morphology and microstructure of the spring fracture,and the spring fracture causes and fracture process were analyzed.Results show that the spring fracture is fatigue failure fracture,and surface microcrack at fatigue source is direct cause of fatigue crack initiation.The surface microcrack is caused by bad shot peening process.The spring factory eliminates the fatigue performance by replacing new steel shot and reducing shot blasting speed.
作者
周斌斌
廖建
彭凯
Zhou Binbin;Liao Jian;Peng Kai(Xinyu Xinsteel Metal Products Co.,Ltd.,Xinyu 338004,China)
出处
《金属制品》
2019年第5期40-42,47,共4页
Metal Products
关键词
弹簧钢丝
拉簧
疲劳断裂
金相组织
裂纹
失效分析
spring wire
tension spring
fatigue fracture
microstructure
crack
failure analysis
作者简介
周斌斌,1984年生,工程师,新余新钢金属制品有限公司技术中心常务副主任;廖建,1988年生,工程师,新余新钢金属制品有限公司钢丝厂技术经理;彭凯,1990年生,工程师,新余新钢金属制品有限公司钢丝厂质量主管。