摘要
研究CuInS 2量子点修饰棉织物的防紫外线性能。制备了多种摩尔浓度的CuInS 2量子点溶液,通过水浴法利用CuInS 2量子点修饰棉织物,分析了CuInS 2量子点修饰棉织物内部结构变化,研究了量子点不同摩尔浓度对棉织物防紫外线性能的影响。结果表明:修饰后棉织物的紫外线吸收率与原织物相比提高了0.5倍~1.8倍,在UVA区域提升尤为明显,UPF可达到50+;量子点与棉织物能形成良好的结合,在水洗12次之后UPF仍达40+。认为:CuInS 2量子点可以有效提高棉织物的防紫外线性能。
Anti-ultraviolet property of CuInS 2 quantum dot modified cotton fabric were studied.Various molar concentrations CuInS 2 quantum dot solution were prepared.Cotton fabric was modified by CuInS 2 quantum dot by water bath method.Internal structure of CuInS 2 quantum dot modified cotton fabric was analyzed.Effect of quantum dot with different molar concentration on cotton fabric anti-ultraviolet property was studied.The results showed that ultraviolet absorption rate of cotton fabric after modification was increased from 0.5 times to 1.8 time s compared with the original fabric.Improvement effect was especially obvious in the UVA region.UPF was reached 50+,combination between quantum dot and cotton fabric was better.After 12 times water washing,UPF was still reached 40+.It is considered that anti-ultraviolet property of cotton fabric can be effectively improved by CuInS 2 quantum dots.
作者
胡泽栋
刘让同
刘淑萍
李亮
耿长军
HU Zedong;LIU Rangtong;LIU Shuping;LI Liang;GENG Changjun(Zhongyuan University of Technology,Henan Zhengzhou,451191;Collaborative Innovation Center of Textiles and Clothing in Henan Province,Henan Zhengzhou,451191;Henan Province Key Laboratory of Functional Textile Materials,Henan Zhengzhou,451191)
出处
《棉纺织技术》
CAS
北大核心
2019年第10期63-66,共4页
Cotton Textile Technology
基金
国家重点研发计划资助项目(2017YFB0309100)
作者简介
胡泽栋(1993—),男,在读硕士研究生;通信作者:刘让同,教授,ranton@126.com。