采用粉末冶金技术制备Ag-34.5Cu-1.5Ti、Ag-26.5Cu-3Ti和Ag-10Cu-4Ti合金材料,用扫描电镜(SEM)、金相显微镜(OM)、差热分析仪(DSC)和润湿角测量仪,表征合金粉末及其材料的形貌、组织结构,研究合金的熔点和与TC4钛合金的润湿性。结果表明,通过真空雾化制粉、冷等静压、真空烧结和轧制等技术集成,可以制备AgCuTi合金材料;合金呈等轴晶组织,金属间化合物呈颗粒状和块状分布。随着钛含量的增加,使得Ag-10Cu-4Ti合金材料的固液相间隔温度最大、润湿角要小于Ag-34.5Cu-1.5Ti和Ag-26.5Cu-3Ti,Ag-10Cu-4Ti材料对TC4钛合金的润湿性能最好。
Ag-34.5Cu-1.5Ti,Ag-26.5Cu-3Ti and Ag-10Cu-4Ti alloys were prepared by powder metallurgy method,and their morphology and microstructure were characterized by using scanning electron microscope(SEM),metallographic microscope(OM),differential scanning calorimeter(DSC)and wetting angle measuring instrument.The melting point of the alloys and the wettability of TC4 titanium alloy were also measured.The results show that AgCuTi alloy can be prepared by combining vacuum atomization,cold isostatic pressing,vacuum sintering and rolling technology integration.Meanwhile,the alloy has equiaxed grain structure and intermetallic compounds are distributed in granular and bulk.With the increase of titanium content,Ag-10Cu-4Ti alloy has the maximum temperature range between the solid and liquid phase with a minimum wetting angle which is smaller than that of Ag-34.5Cu-1.5Ti and Ag-26.5Cu-3Ti.Ag-10Cu-4Ti material has the best wettability on TC4 titanium alloy.
作者
谢明
杜静
魏明霞
高勤琴
何静
陈永泰
王松
杨有才
XIE Ming;DU Jing;WEI Mingxia;GAO Qinqin;HE Jing;CHEN Yongtai;WANG Song;YANG Youcai(Kunming Institute of Precious Metals, State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals, Sino-Platinum Metals Co. Ltd., Kunming 650106, China;AECC Shenyang Liming Aero-engine Co., Ltd, Shenyang 110043, China)
出处
《贵金属》
CAS
CSCD
北大核心
2019年第2期55-58,共4页
Precious Metals
基金
国家重点研发计划(2017YFB0305700)
国家自然科学基金项目(U1602275,U1602271)
云南省重大科技专项(2018ZE011,2018ZE012,2018ZE022,2018ZE026)
云南省应用基础研究计划项目(2018FB088,2017FB144)
关键词
粉末冶金技术
银铜钛合金
组织结构
固液相温度
润湿性
powder metallurgy technology
AgCuTi alloy
microstructure
temperature of solid phase and liquid phase
wettability
作者简介
第一作者:谢明,男,博士,正高级工程师,研究方向:稀贵金属合金材料。E-mail:powder@ipm.com.cn.