Al0.3CrFe1.5MnNi0.5 high entropy alloys(HEA)have special properties.The microstructures and shear strengths of HEA/HEA and HEA/6061-Al joints were determined after direct active soldering(DAS)in air with Sn3.5Ag4Ti active filler at 250°C for 60 s.The results showed that the diffusion of all alloying elements of the HEA alloy was sluggish in the joint area.The joint strengths of HEA/HEA and HEA/6061-Al samples,as analyzed by shear testing,were(14.20±1.63)and(15.70±1.35)MPa,respectively.Observation of the fracture section showed that the HEA/6061-Al soldered joints presented obvious semi-brittle fracture characteristics.
高熵合金Al_(0.3)Cr Fe_(1.5)Mn Ni_(0.5)(HEA)具有许多特殊性能。在大气环境、接合温度为250℃保持60 s的条件下,以Sn3.5Ag4Ti为活性焊料对HEA/HEA及HEA/6061-Al进行直接活性软焊接合,并对其进行显微组织及剪力强度分析。实验结果显示,在接合过程中,高熵合金中所有元素缓慢扩散进入连接区域。HEA/HEA和HEA/6061-Al样品的剪切强度分别为(14.20±1.63)和(15.70±1.35)MPa。HEA/6061-Al样品的断裂面呈显明显的半脆性断裂特征。
基金
financial support of this work from the Ministry of Science and Technology, Taibei, China, under Projects No. MOST 105-ET-E-020002-ET, 105-2622-E-020-003-CC3
作者简介
Corresponding author:L.C.TSAO;Tel:+886-8-7703202 ext.7560;Fax:+886-8-7740552;E-mail:tlclung@mail.npust.edu.tw