对高强度镀锌钢丝的扭转性能和拉拔钢丝的力学性能及微观组织进行研究。力学性能分析表明:扭转性能好的拉拔钢丝的强度和塑性相比扭转性能差的拉拔钢丝无较大差别,然而扭转性能好的拉拔钢丝表面显微硬度比扭转性能差的拉拔钢丝低,波动相对也较平稳。微观组织研究表明:扭转性能差的拉拔钢丝表层组织无半脱碳是其表面硬度较高的主要原因。
In this paper,the torsion properties of high strength galvanized steel wire and the mechanical proper-ties and microstructure of the drawing steel wire were studied.The mechanical properties analysis shows that there is no difference in both of strength and ductility between drawing steel wire with good or poor torsion per-formance.However,the surface hardness value of drawing steel wire with good torsion performance is lower than that of drawing steel wire with poor torsion performance?and the volatility are also relatively more stable.Microstructure research shows that the microstructure of surface layer without semi-decarburization or non-uni-form semi-decarburization of the drawing wire with poor torsion performance is the main reason for the high surface hardness.
作者
乔亚楠
刘新宽
刘平
陈小红
高加强
王军艺
QIAO Yanan;LIU Xinkuan;LIU Ping;CHEN Xiaohong;GAO Jiaqiang;WAMG Junyi(Department of Materials Science and Engineering, University of Shanghai for Science Technology, Shanghai 200093,China;Baoshan Iron Steel Co.,Ltd.,Shanghai 201900,China)
出处
《功能材料》
EI
CAS
CSCD
北大核心
2017年第8期53-57,共5页
Journal of Functional Materials
基金
国家自然科学基金资助项目(51201107)
关键词
镀锌钢丝
拉拔钢丝
表面硬度
脱碳
扭转
galvanized steel wire
drawing steel wire
surface hardness
decarburization
torsion
作者简介
乔亚楠 (１９９１－),女,硕士,师承刘新宽副教授,从事高强度镀锌钢丝扭转破断及显微分析研究.;通讯作者:刘新宽,E-mail:xinkuanliu@163com