Micro-arc oxidation(MAO) technique is capable of producing dense oxide films on the aluminium alloy surface. This oxide film protects the aluminium alloy from the corrosion attack for longer duration.Empirical relationships were derived to evaluate the MAO coating properties(porosity and hardness) by incorporating very important MAO parameters(current density, inter-electrode distance and oxidation time). MAO parameters were also optimized to achieve coatings with minimum porosity and maximum hardness. Further, the effect of MAO parameters on coating characteristics was analysed. From the results, it is found that the current density has greater influence on the responses than the other two parameters.
Micro-arc oxidation(MAO) technique is capable of producing dense oxide films on the aluminium alloy surface. This oxide film protects the aluminium alloy from the corrosion attack for longer duration.Empirical relationships were derived to evaluate the MAO coating properties(porosity and hardness) by incorporating very important MAO parameters(current density, inter-electrode distance and oxidation time). MAO parameters were also optimized to achieve coatings with minimum porosity and maximum hardness. Further, the effect of MAO parameters on coating characteristics was analysed. From the results, it is found that the current density has greater influence on the responses than the other two parameters.
基金
Council of Scientific and Industrial Research (G8/19901/2013), New Delhi for the financial support provided to conduct this investigation through sponsored project No. 22(0615)/13/EMR-II dated 26.02.2013
作者简介
E-mail addresses: jayaraj_kamal@yahoo.co.in (R. Kamal Jayaraj), jeejoo@rediffmail.com (S. Malarvizhi), visvabalu@yahoo.com (V. Balasubramanian).