在影响泡沫混凝土砌块物理和力学性能的众多因素中选出双氧水、水泥、纤维、水胶比四个主导因素进行正交试验设计,结合实际试验经验,提取不同因素的不同水平值,再根据提取的值分组进行配合比试验。将所得的试验结果进行分析,得出泡沫混凝土砌块的最佳配合比为:双氧水掺量、水泥掺量、纤维掺量、水胶比、陶粒掺量、粉煤灰替代水泥掺量、稳泡剂掺量、减水剂掺量、石膏掺量、珍珠岩及纳米CaCO_(3)掺量分别为8.0%、40.0%、0.05%、0.35、25%、35%、1.2%、0.04%、0.05%、3%、0.8%。
Four dominant factors that affect the physical and mechanical properties of foam concrete block are selected by orthogonal experiment design,which are hydrogen peroxide,cement,fiber and water glue ratio.The different values of different factors are extracted with the actual test experience,and the mixture ratio test is carried out according to the extracted value groups.Based on the analysis of the test results,the best mix proportion of foam concrete block is as follows:the content of hydrogen peroxide content,cement content,fiber content,W/B ceramsite content,fly ash replacement cement content,dosage of stabilizer,dosage of water reducing agent,gypsum content,perlite and nano CaCO3 content are respectively 8.0%、40.0%、0.05%、0.35、25%、35%、1.2%、0.04%、0.05%、3%、0.8%.
出处
《混凝土与水泥制品》
北大核心
2018年第10期64-67,共4页
China Concrete and Cement Products
基金
国家自然科学基金资助项目(51768008)
中国博士后科学基金项目(2017M613273XB)
广西自然科学基金项目(2015GXNSFAA139263)
广西科技大学研究生教育创新计划项目
关键词
泡沫混凝土砌块
物理力学性能
正交试验
配合比
Foam concrete block
Physical and mechanical properties
Orthogonal test
Mix proportion
作者简介
邓宇(1978-),男,副教授。联系电话:18077217853,E-mail:dy261@163.com;通讯作者:任吉(1993-),男,硕士。联系电话:15277286083,E-mail:472789495@qq.com