摘要
在阳极和空穴传输层分别引入氧化镍纳米结构缓冲层,制备了蓝色有机发光二极管,对二极管的电学和光学特性进行了测试分析,研究了采用电化学方法制备的氧化镍纳米结构对器件的影响。结果表明,纳米结构氧化镍缓冲层能够有效地提高空穴-电子对的产生和复合效率,它的引入带来了高效的空穴注入及发光层中的载流子平衡,能有效提高有机发光二极管的电致发光特性。氧化镍缓冲层沉积时间为30 s的器件具有最高的亮度和电流效率,分别为42 460 cd/m^2和24 cd/A,该器件的CIEx,y色坐标为(0.212 9,0.325 2)。
The electrical and optical properties of blue organic light-emitting diodes fabricated by utilizing nickeloxide nano buffer layers between the anodes and hole transport layers were investigated.NiO nanolayer on ITO was prepared by the electrochemical methods.The effects of NiO nanolayer on the device performances were studied.The experimental results show that NiO buffer layer can effectively enhance the probability of hole-electron recombination due to an efficient holes injection into and charge balance in an emitting layer.The sample with Ni deposition time of30 s has the highest luminance of 42 460 cd/m^2,maximum current efficiency of 24 cd/A,and CIEx,y coordinates of（0.212 9,0.325 2）,respectively.
出处
《发光学报》
EI
CAS
CSCD
北大核心
2017年第4期492-498,共7页
Chinese Journal of Luminescence
基金
甘肃省自然科学基金(1606RJZA026)
兰州市城关区科技计划(2016cgkj280)资助项目~~
关键词
蓝色有机发光二极管
阳极缓冲层
氧化镍纳米结构
电化学法
blue organic light-emitting diode（BOLED）
anode buffer layers
NiO nanoparticles
electrochemical method
作者简介
孙永哲（1991-），男，河南郑州人，硕士研究生，2013年于兰州大学获得学士学位，主要从事有机半导体器件的研究。E—mail：15117116001@163．com
郑礴（1972-），男，河北保定人，总工程师，1994年于哈尔滨科技大学获得学十学位，主要从事嵌入式技术及仪器仪表方面的研究。E—mail：zhengboem@163．com
李海蓉（1971-），女，甘肃临洮人，博士，教授，2004年于兰州大学获得博士学位，主要从事半导体光电子学方面的研究。E—mail：hdi@lzu．edu．cn