采用不同钠源在醋酸盐燃烧下合成P2结构的Na_(2/3)Ni_(1/3)Mn_(2/3)O_2正极材料。通过XRD、SEM及循环伏安、电化学阻抗谱等测试,分析钠源对材料结构、形貌及电化学性能的影响。以碳酸钠为钠源合成的样品的层状结构较好、颗粒粒径较均一,电化学性能最好。该材料以0.1 C在2.0~4.0 V循环,首次放电比容量为89.8 m Ah/g,库仑效率为123.3%。1.0 C首次放电比容量为74.3 m Ah/g,第50次循环的放电比容量为71.1 m Ah/g,容量保持率为95.7%。
The P2 structure Na2/3Ni1/3Mn2/3O2 cathode material was synthesized with different sodium sources by acetate combustion method.XRD,SEM,cyclic voltammogram and electrochemical impedance spectroscopy were employed to characterize the influence on structure,morphology and electrochemical performance of the materials.The better layered structure,the uniform particle size and the optimal electrochemical performance were achieved for the sample synthesized with Na2CO3 as Na sources.The initial discharge capacity of 89.8 m Ah/g and the coulombic efficiency of 123.3% at 0.1 C in 2.0-4.0 V.The initial discharge capacity was 74.3 m Ah/g at 1.0 C,the discharge capacity was 71.1 m Ah/g and the capacity retention was 95.7% after 50 cycles.
出处
《电池》
CAS
CSCD
北大核心
2017年第1期12-15,共4页
Battery Bimonthly
作者简介
陈森（1990-），男，山西人，河北工业大学化工学院硕士生，研究方向：应用电化学；
韩恩山（1963-），男，山东人，河北工业大学化工学院教授，博士，研究方向：应用电化学，本文联系人
朱令之（1963-），女，山东人，河北工业大学化工学院副教授，博士，研究方向：应用电化学；
许寒（1982-），男，河北人，中国电子科技集团第十八研究所高级工程师，博士，研究方向：应用电化学。