摘要
通过合金制备、组织观察和拉伸实验,研究了Y和Sm对镁合金AZ81组织和力学性能的影响。结果表明,适量的Y和Sm加入镁合金AZ81后可生成高熔点的Al2Y和Al2Sm相,从而细化晶粒,改善组织。在室温和150℃下,合金的抗拉强度和伸长率均随着Y和Sm总含量的增加先升高后降低,其中,Y和Sm总含量为1.8%(质量分数)时,合金的力学性能最好。
The effect of rare earth elements Y and Sm on the microstructure and mechanical properties of magnesium alloy AZ81 has been investigated by alloy preparation,microstructure observation and tensile tests. The results show that the formation of Al2 Y and Al2 Sm phases with high melting point is observed in magnesium alloy AZ81 after proper addition of Y and Sm. It leads to grain refinement and microstructure improvement of the alloy. With the increase of Y and Sm addition,the tensile strength and elongation of the alloy at room temperature and 150℃ increase at first and then decrease,and reach the peak value at 1. 8wt% Y and Sm.
出处
《稀土》
EI
CAS
CSCD
北大核心
2017年第1期143-147,共5页
Chinese Rare Earths
基金
国家自然科学基金项目(NSFC-河南人才培养联合基金U1404501)
河南省科技攻关重点项目(102102210087)
关键词
镁合金
稀土
组织
力学性能
magnesium alloy
rare earth
microstructure
mechanical properties
作者简介
李萍（1978-），女，河南洛阳人，硕士，主要从事工程力学和材料学研究。
通讯联系人（E-mail：jgxwangying@126．com）