摘要
分别利用分光光度计和紫外成像系统对紫外滤光片的性能进行测试,通过这两项测试数据来评价滤光片的整体性能。所研制的滤光片透过率峰值可在250~280nm范围间进行调节,峰值透过率可达到25%以上,带宽20nm左右。紫外成像系统正对太阳的噪点小于20个/秒,能有效地吸收干扰光。另外测试表明研制的滤光片具有可靠性高、环境适应性强的特点,具有良好的应用性能。
The transmission spectrum of the ultraviolet filter was measured by using spectrophotometry and the solar blind characteristic of the filter was analyzed by the system of detecting UV images.The position of the transmittance peak could be adjusted between 250 and 280nm,the peak transmittance could reach higher than 25%and the bandwidth is about 20 nm.The filter shows strong absorbing ability in the region between 290 nm and 1100 nm.Blocks PMT exposure to direct sunlight is fewer than 20 photons per second.The test results show that the filter has good performance in application.
作者
颜士飞
王葵
赵文锦
李拂晓
袁志耀
钟伟俊
赵凤玲
YAN Shifei WANG Kui ZHAO Wenjin LI Fuxiao YUAN ZhiYao ZHONG Weijun ZHAO Fengling(The 55th Research Institute of China Electronics Technology Group Corporation, Nanjing 210016, CHN)
出处
《光电子技术》
CAS
2016年第4期260-264,共5页
Optoelectronic Technology
作者简介
颜士飞（1984-），男，工程师，主要从事功能性材料和真空光电探测器件研究与开发；（E-mail：yanshifei．2004@163．com）
王葵（1967-），女，教授级高级工程师，研究方向为真空光电探测器件的研制和开发；
赵文锦（1965-），女，教授级高级工程师，研究方向为真空光电探测器件的研制和开发。