以四氯化钛、硫脲、有机羧酸、氨水、D-山梨醇等为主要实验原料,常温常压条件下采用新型络合-控制水解法制备S掺杂纳米TiO_2透明溶胶,该溶胶的平均粒径为4.1nm.使用XRD、纳米激光粒度分析仪、UV-Vis表征样品的物相、粒径、吸收光谱和光催化性能.此外,还对合成过程中反应条件对结果的影响进行了研究.结果表明,S掺杂质量分数为0.5%,回流时间为15min时,S掺杂纳米TiO_2透明溶胶的光催化性能达到最优.
Sulfur-doped nganic carboxylic acid,NH3 hydrolysis method at roomano TiO2 transparent hydrosol was synthesized by using TIC14, thiourea, or-H20,D-sorbitol etc. as raw materials, through a novel complexation-controlledtemperat4.1 nm. The phase structure, particleure and atmospheric pressure. The hydrosol average particle size is size, composition, absorbance spectrum, and photocatalytic perform-ance of samples were characterized by XRD,nano laser particle size analyzer and ultraviolet-visible spectro-photometer. Furthermore, the effect of reaction conditions on the synthesis process was also studied. Theresults show that the photocatalytic performance of sulfur-doped Ti02 hydrosol was optimal when the do-ping content of S was 0.5%and the reflux time was 15 min.
出处
《河北大学学报（自然科学版）》
CAS
北大核心
2016年第2期124-128,共5页
Journal of Hebei University(Natural Science Edition)
基金
国家自然科学基金资助项目(21201053)
高等学校博士学科点专项科研基金新教师类资助项目(20121301120005)
河北省自然科学基金资助项目(F2014201078)
河北省应用基础研究计划重点基础研究项目(14964306D)
河北大学引进人才启动基金资助项目(2012-233)
河北大学学生综合素质培养项目(2015zh0442
2015zh0443)
河北省大学生创新创业训练计划项目(2015066
2015064
201510075047:026)
河北省自然科学基金资助项目(2015201050)
河北省教育厅基金资助项目(QN2014057)
河北省教育厅重点项目基金(ZD2016055)
河北省大学杰出青年基金资助项目(2015JQ02)
河北省研究生创新资助项目(S2016023)
关键词
纳米TiO2透明溶胶
S掺杂
最小粒子直径
光催化
nano-TiO2 transparent hydrosol
sulfur-doped
minimum particle diameter
photocatalysis
作者简介
第一作者：王明坤（1991-），女，河北邢台人，河北大学在读硕士研究生．E-mail：wmk-1234@126．com
通信作者：李玲（1980-），女，河北保定人，河北大学副教授，博士，主要从事纳米材料及太阳能电池研究．E—mail：lilinghbu@163．COm