700MPa级高强度低合金热轧铁素体钢带强化机制 被引量:11

Strengthening mechanism of 700 MPa grade high strength low alloy hot rolled ferritic steel strip
原文传递
导出
摘要 700 MPa级高强度低合金热轧铁素体钢带作为一类新型的低成本结构材料,在泵车、起重机等工程机械行业得到广泛应用。为了明确这类钢种的强化机制,选取典型热轧带钢TS700MC作为试验材料,采用拉伸试验、夏比冲击试验测定其强度和韧性,用OM、SEM、TEM表征其微观组织。结果表明,TS700MC的屈服强度和抗拉强度为715和825 MPa,伸长率为18.5%,-40℃的夏比冲击值为104 J,且韧脆转变温度不大于-40℃。微观组织接近于全铁素体,晶粒平均尺寸约为3.4μm,且含有高密度的位错。大量纳米级的(Ti,Nb,Mo)(C,N)粒子沿位错和晶内析出。高强度是固溶强化(约16%),细晶强化(约38%),析出强化和位错强化(约46%)等多种强化机制综合作用的结果。 As a novel kind of low-cost structural materials,700 MPa grade high strength low alloy hot rolled ferritic steel strip has been widely used in the construction machinery industry,such as pumps,cranes in recent years. In the current study,to understand the strengthening mechanism,a typical strip steel TS700MC was selected as experimental material. Tensile test and charpy impact test were used to evaluate the strength and the toughness,the microstructure was characterized by OM,SEM and TEM. The results showed that the yield strength,the tensile strength,the elonga-tion and the charpy impact value at-40℃of TS700MC were 715,825 MPa,18.5%,104 J,respectively. The charpy fracture appearance transition temperature was lower than-40℃. Virtually fully ferritic microstructure was obtained, and the average grain size was approximately 3.4μm. High-density dislocations existed in the microstructure. Lots of na-no-sized (Ti,Mo,Nb)(C,N) particles precipitated along the dislocation and in the matrix. The high strength results from a combination of solid solution hardening (about 16%),grain refinement hardening (about 38%),precipitation and dislo-cation hardening (about 46%).
出处 《钢铁》 CAS CSCD 北大核心 2016年第3期78-83,共6页 Iron and Steel
关键词 700MPa级 铁素体钢 热轧 钢带 超细晶 强化机制 700 MPa ferritic steel hot rolled steel strip ultra-fine grain strengthening mechanism
作者简介 付培茂(1969-),男,大学本科,工程师;E-mail:fupm@tisco.com.cn
  • 相关文献

参考文献11

  • 1Kashima T, Mukai Y. Development of 780 MPa class high strength hot rolled steel sheet with super high flange formability [J]. R&D Kobe Steel Engineering Reports, 2002, 52(3): 19.
  • 2Misra R D K, Nathani H, Hartmann J E, et al. Microstructural evolution in a new 770 MPa hot rolled Nb-Ti microalloyed steel [J]. Materials Science and Engineering: A, 2005, 394(1/2): 339.
  • 3章洪涛,刘成彬,庞干云.太钢生产的高强度热轧带钢S700MC试验报告[R].太原:太原钢铁(集团)有限公司,2009,16.
  • 4Craven A J, He K, Garvie L A J, et al. Complex heteroge- neous precipitation in titanium-niobium microaUoyed Al-killed HSLA steels-I(Ti, Nb)(C, N)particles[J]. Acta Materialia, 2000, 48(15): 3857.
  • 5Lee W B, Hong S G, Park C G, et al. Influence of Mo on pre- cipitation hardening in hot rolled HSLA steels containing Nb [J]. Scripta Materialia, 2000, 43(4): 319.
  • 6Jang J H, Heo Y U, Lee C H, et al. Interphase precipitation in Ti-Nb and Ti-Nb-Mo bearing steel[J]. Materials Science and Technology,2013, 29 (3): 309.
  • 7Wenjin Nie, Shanwu Yang, Shaoqiang Yuan, and Xinlai HeMaterials Science and Engineering School, University of Science and Technology Beijing, Beijing 100083, China.Dissolving of Nb and Ti carbonitride precipitates in microalloyed steels[J].Journal of University of Science and Technology Beijing,2003,10(5):78-80. 被引量:8
  • 8Timokhina I B, Hodgson P D, Ringer S P, et al. Precipitate characterisation of an advanced high-strength low-alloy(HSLA) steel using atom probe tomography[J]. Scripta Materialia, 2007, 56(7): 601.
  • 9章洪涛,刘成彬,庞干云.太钢高强度微合金热轧带钢TH800钢的性能,显微组织和析出相[R].太原:太原钢铁(集团)有限公司,2008,46.
  • 10Charleux M, Poole W J, Militzer M, et al. Precipitation behav- ior and its effect on strengthening of an HSLA-Nb/Ti steel[J]. Metallurgical and Materials Transactions: A, 2001,32(7): 1635.

共引文献7

同被引文献81

引证文献11

二级引证文献50

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部