摘要
橡胶颗粒以代替部分细集料的形式掺入再生沥青混合料中,分别制备成不同橡胶颗粒粒径下橡胶颗粒掺量为0、1%、2%和3%的再生橡胶颗粒沥青混合料进行马歇尔试验。试验结果表明:掺加小粒径橡胶颗粒的再生橡胶颗粒沥青混合料的最佳橡胶颗粒掺量为1.5%,其相应的新沥青掺量为4.12%;掺加大粒径橡胶颗粒的最佳橡胶颗粒掺量为1.2%,其相应的新沥青掺量为4.93%,且其马歇尔力学指标值低于掺加小粒径橡胶颗粒的再生混合料。小粒径的橡胶颗粒更适合作为再生沥青混合料的外掺物。
Rubber particles are added into the recycled asphalt mixture as replacement of particle fine aggregate,and recycled rubber particles asphalt mixture is prepared by the different size and addition amount of 0,1%,2%and 3%rubber particles to carry out the Marshall test.The test results show that：the best rubber particles content of the small rubber particles is 1.5%,the corresponding new asphalt content is 4.12%;the best rubber particles content of the big rubber particles is 1.2%,the corresponding new asphalt content is 4.93%;and its mechanics indexes are lower than adding particle size of rubber particles.The small particle rubber size as recycled asphalt mixture is more suitable for the additive content.
出处
《公路》
北大核心
2016年第3期154-159,共6页
Highway
基金
国家自然科学基金项目
项目编号51168042
塔里木大学校长基金创新群体研究项目
项目编号TDZKPY201401
大学生创新创业训练计划国家级项目
项目编号201410757003
关键词
道路工程
橡胶颗粒
再生沥青混合料
马歇尔试验
road engineering
rubber particles
recycled asphalt mixture
Marshall test