摘要
基于高强抗震钢筋的基本特征,介绍了微合金化、余热处理及细晶化技术在生产高强抗震钢筋中的应用。微合金化技术相对于其他两种应用更为广泛,余热处理和细晶化技术比微合金化成本低,无需添加合金元素,且能满足钢筋的抗震性能。通过对3种工艺的综合分析,提出在生产高强抗震钢筋时,应当将微合金化与余热处理结合起来,这样不仅节约生产成本,还有利于提高钢筋的抗震性能。
The application of the micro-alloying, quenched and self-tempered （QST） and fine-grained technolo- gies in high-strength aseismic reinforcement steel bars are introduced, based on characteristics of high-strength aseis- mic reinforcement steel bars. Micro-alloying technology is more widely used than the other. The cost of the QST and fine grained technology without adding alloying elements is lower than the micro-alloying and can also meet the seismic performance o{ steel bars. The compTehensive analysis of three processes shows combining micro-alloying with QST in the production of high-strength aseismic steel bars can reduce the production cost and improve the seismic perfor- mance.
出处
《材料导报》
EI
CAS
CSCD
北大核心
2015年第19期101-104,110,共5页
Materials Reports
基金
陕西省教育厅服务地方专项计划项目(14JF013)
关键词
高强抗震钢筋
微合金化
余热处理
细晶化
high-strength reinforcement, micro-alloy, quenched and self-temper, fine-grain
作者简介
杨雨晴：女，1989年生，硕士生，研究方向为材料工程E-mail：287456390@qq．com
王庆娟：通讯作者，女，1973年生，博士，教授，研究方向为冶金技术及钢材轧制工艺技术E-mail：jiandawqj@163．com