摘要
The present work aims to compare the amorphous phase forming ability of ternary and quaternary Al based alloys （Al86Ni8Y6, Al86GNi6Y6Co2, Al86NigLa6 and Al86Ni8Y45La15） synthesized via mechanical alloying by varying the composition, i.e. fully or partially replacing rare earth （RE） and transition metal （TM） elements based on similar atomic radii and coordination number. X-ray diffraction and high resolution transmission electron microscopy study revealed that the amorphization process occurred through formation of various intermetallic phases and nanocrystalline FCC Al. Fully amorphous phase was obtained for the alloys not containing lanthanum, whereas the other alloys containing La showed partial amorphization with reappearance of intermetallic phases attributed to mechanical crystallization. Differential scanning calorimetry study confirmed better thermal stability with wider transformation temperature for the alloys without La.
The present work aims to compare the amorphous phase forming ability of ternary and quaternary Al based alloys （Al86Ni8Y6, Al86GNi6Y6Co2, Al86NigLa6 and Al86Ni8Y45La15） synthesized via mechanical alloying by varying the composition, i.e. fully or partially replacing rare earth （RE） and transition metal （TM） elements based on similar atomic radii and coordination number. X-ray diffraction and high resolution transmission electron microscopy study revealed that the amorphization process occurred through formation of various intermetallic phases and nanocrystalline FCC Al. Fully amorphous phase was obtained for the alloys not containing lanthanum, whereas the other alloys containing La showed partial amorphization with reappearance of intermetallic phases attributed to mechanical crystallization. Differential scanning calorimetry study confirmed better thermal stability with wider transformation temperature for the alloys without La.
基金
financial support obtained from the Science and Engineering Research Board,Department of Science & Technology,Government of India(SB/S3/ME/0044/2013)
Sponsored Research and Industrial Consultancy,Indian Institute of Technology Kharagpur,India(GAF)
作者简介
Corresponding author. Ph.D.; Tel.： ＋91 3222 283242; Fax： ＋91 3222 282280. E-mail address： laha@metal.iitkgp.ernet.in （T. Laha）.