摘要
对55%变形条件下冷轧复合4A60铝/08Al钢复合带材进行退火处理,研究退火温度对钢层再结晶行为和铝-钢界面结合强度的影响。结果表明,退火温度为600℃保温60 min,钢层发生完全再结晶;退火温度为400~600℃,保温60 min,铝-钢复合板界面结合强度达到最大值9 N/mm,当保温时间为60 min,温度高于610℃时,铝-钢界面处产生脆性化合物,结合强度急剧降低至2.7 N/mm。确定55%变形条件下铝-钢复合板最佳退火工艺为600℃保温60 min。
4A60（ Al） /08Al（ steel） clad strips bonded by cold rolling were annealed after 55% reduction. The effect of annealing temperature on the steel recrystallization behavior and bonding strength at Al-steel interface was investigated. The results show that the steel recrystallized completely by annealing at 600 ℃ for 60 min. When the annealing temperature is 400-600 ℃ and holding for 60 min,the bonding strength at the Al-steel interface reaches maximum. 9 N / mm. However,when the holding time remains 60 min,and the annealing temperature exceeds 610 ℃,the intermetallic compounds appear at the Al-steel interface,and the bonding strength decreases from 9 N / mm to 2. 7 N / mm rapidly. The optimum annealing process of Al-steel clad strips is to anneal at 600 ℃ for 60 min with 55% reduction.
出处
《金属热处理》
CAS
CSCD
北大核心
2015年第10期72-75,共4页
Heat Treatment of Metals
基金
国家高技术研究发展计划(863计划)(2013AA031301)
国家国际科技合作专项项目(2013DFB50170)
江苏省科技成果转化专项资金项目(BA2011038)
江苏重点实验室资助项目(BM2014006)
关键词
再结晶
结合强度
退火工艺
铝-钢复合板
recrystallization
bonding strength
annealing process
Al-steel clad strips
作者简介
作者简介：张小军（1987-），男，硕士，主要进行金属复合材料研发工作，联系电话：0510-88990831，E-mail：xiaojun．zhang@cn-yinbang，com。
通讯作者：周德敬，教授级高工，E-mail：dejing．zhou@cn-yinbang．com.