通过电化学测试研究了N-(4-磺酸基丁基)三乙基铵硫酸氢盐([(CH2)4SO3HTEA][HSO4])酸性离子液体在25℃、0.5mol/L的HCl溶液中对Q235钢的缓蚀性能。结果表明,该离子液体在一定的浓度范围内能够减缓HCl溶液对Q235钢的腐蚀,当离子液体的浓度为14mmol/L时,缓蚀效果最好。X射线光电子能谱(XPS)表征结果表明,在Q235钢表面离子液体能够形成吸附保护膜,覆盖反应活性中心,减缓HCl溶液对Q235钢的腐蚀。
Corrosion inhibition effect of N-（4-sulfonic acid）butyl triethylammonium hydrogen sulfate（[（CH 2 ）4 SO 3 HTEA] [HSO 4 ]）acid ionic liquid（IL）towards Q235 steel corrosion in 0.5 mol/L HCl solution was investigated by electrochemical measurements in 25 ℃.The results show that the IL suppressed corrosion processes of Q235 steel in HCl solutionand the best performance of inhibition could be obtained with the concentration of inhibitor 14 mmol/L.The X-ray photoelectron spectroscopy（XPS）demonstrates that the protectiue film is formed by adsorption on the Q235steel surface,which can cover the reative center and inhibit the Q235 steel corrosion in HCl solution.
出处
《辽宁石油化工大学学报》
CAS
2015年第2期17-21,31,共6页
Journal of Liaoning Petrochemical University
基金
国家自然科学基金项目(21103077)
新世纪优秀人才支持计划项目(NCET-11-1011)
辽宁自然科学基金项目(201102120
201202123)
作者简介
李明丽（1989-），女，硕士研究生，从事离子液体在缓蚀剂中的应用的研究；E-mail：mingli423@163．com。
通信联系人：张磊（1983-），男，博士，讲师，从事催化剂及催化反应工程的研究；E-mail：lnpuzhanglei@163.com。