以全密封镉镍电池为研究对象,从镉镍电池的基板、镍正极、镉负极等9个方面着手,对可导致全密封镉镍蓄电池失效的因素进行了系统地阐述与分析,并针对相应的失效原因提出了相应的预防措施及改善方法。
The failure mode and effect analysis （FMEA） of hermetically sealed cadmium-nickel cell from 9 factors was investigated, including plate, nickel-hydroxide electrode, cadmium-hydroxide electrode, separator, and et al. The failure factors of cadmium-nickel cell were also systematically analyzed. According to the failure factors, some relevant preventive measure and improving methods were proposed.