向WC陶瓷镍基合金粉末中添加不同质量分数的La2O3粉末制成混合粉末,采用大功率半导体激光器通过同轴送粉方式,在A3钢基材上制备熔覆层。利用SEM、EDAX、XRD分析研究了不同稀土加入量对熔覆层显微组织和相结构的影响,用显微硬度计、滑动摩擦磨损试验机分别测试了复合涂层的硬度、耐磨性。结果表明:由于稀土的加入,复合涂层的晶粒进一步细化,组织趋向均匀,硬度和耐磨性得到了提高,最终得出涂层粉末的最佳配比为(质量分数)59%Ni60,40%WC,1.0%La2O3。
Abstract： WC/Ni-based composite coatings added with different contents of La2 O3 were clad on A3 steel substrates by high power semiconductor laser with Auto-Sync powder feeding system. The effect of different contents of La3 O3 on the microstructure and phase structure of WC/Ni-based composite coating was investigated by scanning electron microscope （SEM）, energy-dispersive analysis of X-rays（EDAX） ,X-ray diffraetion（XRD）. The microhardness and wear resistance of the coatings were measured by microhardness tester and friction-wear tester. The results revealed that with the addition of La2 O3, the microstrueture of the coatings was refined, purified and become well-distribu- ted, the microhardness and wear resistance of the coatings were improved.
出处
《金属功能材料》
CAS
2014年第4期14-17,共4页
Metallic Functional Materials
作者简介
王震（1988-），男，硕士；E-mail：wangzhen5473@emails．bjut．edu．cn；