摘要
TiAl金属间化合物具有低密度、高弹性模量、高比强度、良好的抗高温蠕变和抗高温氧化性能,被认为是极具潜力的高温结构材料,在航空航天及汽车发动机领域具有广阔的应用前景,特别是经定向凝固得到的TiAl合金在综合力学性能方面可得到良好的配合。然而,TiAl合金熔体由于具有高的化学活性,会与所有已知的耐火材料发生不同程度的化学反应,限制了其定向凝固铸件的生产和应用。首先回顾了TiAl合金的熔炼技术,然后对TiAl合金精密铸造及定向凝固用耐火材料的研究现状进行了总结,在此基础上提出了一种新型的TiAl合金定向凝固用BaZrO3耐火材料,并展望了其今后的发展。
Because of the low density, high Young＇s modulus, high specific strength and good oxidation resis- tance and creep resistance at elevated temperatures, TiA1 alloys have been extensively studied and considered as poten- tial high temperature structural materials for the aerospace and automotive industries, especially the directional solidi- fied TiAI alloys can get a good balance of mechanical properties. However, the high reactivity between the molten al- loys and the commercial ceramic crucible materials has prevented the future application. A brief history of melting technology of TiA1 alloys is reviewed and then a summary about the development of refractories used in precision cas- ting and directional solidification of TiA1 alloys is presented. solidification of TiAI alloys is mentioned, its future direction is also discussed.
出处
《材料导报》
EI
CAS
CSCD
北大核心
2014年第15期87-92,103,共7页
Materials Reports
基金
上海市科委基金(11520500100
11DZ2283400)
国家自然科学基金(51225401
51374142)
钢铁冶金新技术国家重点实验室开放课题(KF12-05)
作者简介
贺进：男，1989年生，硕士生，主要从事TiAi合金定向凝固研究
鲁雄刚：男，博士，教授，主要从事治金新工艺的研究和开发Tel：021-56335768E-mail：luxg：@staff．shu．edu．cn
李重河：通讯作者，男，博士，教授，研究方向为材料设计、新材料研制、计算材料学Tel：021-56332934E-mail：chli@staff．shu．edu．cn