采用共沉淀法制备了一系列复合催化剂Fe-Cu-Al-K,并对这些复合催化剂加氢催化CO2制备液态烃的催化性能进行了研究;通过XRD、TEM、BET、H2-TPR和CO2-TPD等分析方法对催化剂进行了表征。研究结果发现,Cu渗入到了Fe的晶格内,Cu的加入有助于催化剂比表面积的增加和CO2吸附量的提高,并促进了催化剂的还原过程。催化性能测试结果表明:在300℃、2 MPa、空速2 000 mg/[g(cat.)·h]和H2/CO2摩尔比为3的条件下,Cu的加入有助于获得较高的催化活性和油相产率,并有利于油相中碳链较长的液态烃的生成。当Cu质量分数为6.6%时,催化效果最好,转化率为34.58%,C+6选择性为29.26%,油相产率为10.7 mg/[g(cat.)·h]。
A series of composite Fe-Cu-A1-K catalysts with different Cu content are prepared by co-precipitation method.The hydrogenation of CO2 to liquid hydrocarbons is investigated.The catalysts are characterized by XRD,TEM,BET surface area,H2-TPR and CO2-TPD.The results show that the Cu has doped into the Fe2 O3 crystals.The addition of Cu increases the surface area and CO2 adsorption capacity,as well as promotes the reduction of the catalysts.The reaction test is under the condition of 300℃,2 MPa,2 000 mg/[g（cat.） ·h] of space velocity and 3 of n（H2/CO2）.When Cu content is 6.6％,the catalyst shows the best catalytic performance.The conversion and selectivity of C6＋ are 34.58％ and 29.26％,respectively.The oil yield is 10.7 mg/[g（cat.） ·h].
出处
《现代化工》
CAS
CSCD
北大核心
2014年第8期61-66,共6页
Modern Chemical Industry
基金
国家自然科学基金(21176142)
教育部清华大学自主科研计划(20111081067)
关键词
CO2加氢
液态烃
铁基催化剂
铜助剂
CO2 hydrogenation
liquid hydrocarbon
Fe-based catalyst
Cu-promoted catalyst
作者简介
杨铮（1989-）,男,硕士生,研究方向为低品位碳资源的利用,yangzheng123456789@sina.com
吴玉龙（1972-）,男,博士,副教授,硕士生导师,研究方向为资源高效利用过程中的化工技术,通讯联系人,wylong@tsinghua.edu.cn.