摘要
用 ESR方法研究了一种纳米 Zr O2 在普通 H2 气中升温条件下的表面效应 . Zr O2 上 Zr3+ 的中心量约为 1× 1 0 - 7mol/g.这些 Zr3+ 中心是 Zr O2 表面一些 O2 - 配位不饱和的 Zr原子点位 .在普通 H2 气中 ,Zr O2 上的 Zr3+ 中心数在温度低于 40 0℃时变化很小 .但在这一温度范围内从室温升温时 ,由 Zr O2 表面羟基的 H2还原引起的 F中心量随温度的升高而增加 .温度高于 40 0℃时 ,Zr O2 表面的 Zr3+及 F中心可与普通 H2 气中存在的少量 O2 气作用产生 O- 2 ,并伴随 Zr O2 表面羟基的脱除而形成新的 Zr3+ .
A kind of ZrO 2 nanopowder annealed at different temperatures in H 2 has been studied by ESR. On the surface of ZrO 2, about 1×10 -7 mol/g of Zr 3+ centers are detected, which are the oxygen coordinatively unsaturated Zr. When the annealing temperature is lower than 400 ℃, the amount of Zr 3+ center remains almost unchanged, while the amount of F center increases in this temperature range, which may be resulted from the reduction of surface hydroxyl by H 2. When the annealing temperature is higher than 400 ℃, O - 2 is originated on the surface of ZrO 2, which may be formed from the reaction of Zr 3+ and F center with the trace amount of O 2 in ordinary H 2, and simultaneously, some Zr 3+ centers are created, as being accompanied with the removal of surface hydroxyl.
出处
《高等学校化学学报》
SCIE
EI
CAS
CSCD
北大核心
2002年第7期1343-1346,共4页
Chemical Journal of Chinese Universities
基金
国家自然科学基金 (批准号 :2 99770 4)