摘要
研究了二聚酸二缩水甘油酯及其改性胺环氧固化剂的制备工艺,制得具有增韧作用的环氧树脂固化剂。采用羧酸-环氧氯丙烷(ECH)酯化、闭环二步法合成二聚酸二缩水甘油酯,其最佳合成工艺条件为:催化剂为四丁基溴化铵且用量为二聚酸(DA)质量的2%,酯化反应温度为90℃,DA∶ECH(摩尔比,下同)=1∶10,环化反应温度为55℃,NaOH质量分数为30%,DA∶NaOH=1∶4。将制得的缩水甘油酯与异佛尔酮二胺进行胺化反应得到改性胺固化剂,其与环氧树脂618固化产物的冲击强度为29.6kJ/m^2,体现出优异的增韧效果。
The preparation process of dimer acid diglycidyl ester and its modified amine epoxy curing agent was investigated,and the epoxy resin curing agent with toughening effect was prepared.Dimer acid diglycidyl ester was prepared by using two-step synthesis of carboxylic acid-epichlorohydrin esterification and dehydrohalogenation.The optimum synthesis conditions were as follows:tetrabutylammonium bromide was used as catalyst and its amount was2% of DA weight.The esterification reaction temperature was 90℃,DA∶ECH(molar ratio)=1∶10,the cyclization reaction temperature was 55℃.the concentration of sodium hydroxide(NaOH)was 30%(weight),DA∶NaOH(molar ratio)=1∶4.The obtained glycidyl ester and isophorone diamine were subjected to amination reaction to obtain modified amine curing agent.The impact strength of product cured by epoxy resin 618 and the modified amine curing agent was29.6 kJ/m^2,which showed that the curing agent had excellent toughening effect.
作者
童伟
何辛
高晟弢
王蓉
周心怡
吴蓁
Tong Wei;He Xin;Gao Shengtao;Wang Rong;Zhou Xinyi;Wu Zhen(School of Materials Science and Engineering,Shanghai Institute of Technology, Shanghai 201418;Shanghai Resin Factory,Shanghai 200336)
出处
《化工新型材料》
CAS
CSCD
北大核心
2019年第1期177-180,共4页
New Chemical Materials
基金
上海市教育基金(LM201713)
上海应用技术大学绿色涂料协同创新平台建设资助(3921NH166015)
关键词
缩水甘油酯
改性胺固化剂
环氧树脂
增韧
glycidyl ester
modified amine curing agent
epoxy resin
toughening
作者简介
童伟(1992-),女,硕士,主要从事功能高分子材料、环氧树脂及其固化剂的研究;联系人:吴蓁,男,教授,硕士研究生导师,主要研究方向为高分子液态树脂合成、复合改性及应用。