为研究高温烧结羟基磷灰石靶的细胞相容性,把纯度为99%的羟基磷灰石粉末压制成圆盘形靶,在氩气中于800℃高温下烧结成型。用X射线衍射仪和X射线光电子能谱仪对羟基磷灰石靶的结构组成进行检测。用四氮唑盐比色法对羟基磷灰石靶的细胞相容性进行检测,检测结果表明:纯度为99%的羟基磷灰石粉末在压制成型和800℃高温烧结的过程中化学组成没有发生变化,羟基磷灰石靶中的平均粒径为78.2 nm,结晶度为89.4%,Ca/P比值为1.592;具有很好的细胞相容性。
In order to investigate cellular compatibility of hydroxyapatite（HA） target sintered at high temperature,the powder of 99%pure hydroxyapatite was pressed to discal targets and the targets were sintered at 800℃ in argon ambience.The microstructure and composition of targets were detected with X-ray diffractometer（XRD） and X-ray photoelectron spectroscopy（XPS）.The cellular compatibility of targets was detected with methyl thiazolyl tetrazolium（MTT）.The experimental result demonstrates the chemical composition of targets was not changed while the powder of hydroxyapatite was pressed to targets and the targets were sintered at 800℃ in argon ambience.The average particle diameter in target was 78.2 nm,the crystallinity in target was 89.4%and the ratio of Ca to P in target was 1.592.The hydroxyapatite target sintered at 800℃ had cellular compatibility.
出处
《量子电子学报》
CAS
CSCD
北大核心
2014年第3期368-371,共4页
Chinese Journal of Quantum Electronics
基金
安徽省自然科学基金(1308085MF104)
关键词
材料
羟基磷灰石靶
高温烧结
钙磷比
细胞相容性
materials
hydroxyapatite target
sintering at high temperature
ratio of Ca to P
cellular compatibility
作者简介
罗乐（1963-），安徽淮南人，博士，副教授，主要从事激光技术与生物功能薄膜材料的研究。E-mail：luolehfut@sina．com