摘要
基于水泥乳化沥青砂浆充填层服役环境条件，测试了干燥、气干以及饱水状态下CRTSI型水泥乳化沥青砂浆在-20～60℃时的热变形．结果表明：湿含量对水泥乳化沥青砂浆的热变形行为具有显著影响，非干燥状态水泥乳化沥青砂浆的热变形是自身组分热变形、内部水相态转变及蒸发所导致的体积变形的综合表现；在升温过程中，水泥乳化沥青砂浆内部水向外迁移引起显著的收缩变形，这种收缩变形导致非干燥状态水泥乳化沥青砂浆在20℃左右出现热收缩现象；在饱水条件下，冰一水相变产生的体积收缩导致水泥乳化沥青砂浆在-5～5℃时产生显著的收缩．
In order to know influence of inner moisture on thermal deformation of cement and emulsified-as- phalt mortar, change in length of specimens under different inner moisture conditions, namely vacuum dried, air dry and water saturated, was measured from --20 ℃ to 60 ℃. Results show that the inner mois- ture has a significant influence on thermal deformation of cement and emulsified-asphalt mortar. The evap- oration of inner moisture causes shrinkage notably as temperature rises. This shrinkage reduces its thermal expansion coefficient and can even lead to a negative thermal expansion around 20 ℃. In the case of water saturated condition, the transition of inner moisture from ice to liquid water between --5 and 5 ℃ results in another negative thermal expansion, too.
出处
《建筑材料学报》
EI
CAS
CSCD
北大核心
2013年第5期817-823,828,共8页
Journal of Building Materials
基金
国家自然科学基金资助项目(50978257)
国家重点基础研究发展计划(973计划)项目(2013CB036201)
关键词
水泥乳化沥青砂浆
湿含量
热变形
热收缩
cement and emulsified-asphalt mortar
moisture content
thermal deformation
thermal shrinkage