摘要
采用化学共沉淀法制备尖晶石型ZnFe2O4纳米颗粒,将所得产物在450～900℃焙烧4h,使用FT-IR、XRD、TG-DTG、HRTEM及VSM研究烧结温度对化学成分、微结构及磁化性能的影响。研究结果表明:随着烧结温度升高,ZnFe2O4纳米颗粒尺寸从14nm增大到了50nm,而磁化强度从3.374emu/g降低到了2.168emu/g。
The spinel structured zinc ferrite （ZnFe2O4） nanoparticles were synthesized using corecipitation route. Then the nanoparticles were sintered at various temperatures from 450 ℃ to 900 ℃for 4 h. The effects of heat treatment temperature on crystalline phase formation microstructure and magnetic properties Zn ferrite were investigated by FT-IR, XRD, TG-DTG, HRTEM and VSM. The results show that with the increase of the sintered temperature the average particles size increasing from 14 nm to 50 nm and the M decrease from 3. 374 emu/g to 2. 168 emu/g.
出处
《材料导报》
EI
CAS
CSCD
北大核心
2013年第10期57-59,共3页
Materials Reports
基金
国家教育部博士点基金(20113120110005)
上海市纳米专项资助(1052nm02900)
关键词
纳米锌铁氧体
热处理
微结构
磁性能
zinc ferrite nanoparticles, heat treatment, microstructure, magnetic property
作者简介
张永刚：男，1986年生，硕士生，从事纳米铁氧体材料制备及光催化性能研究E-mail：yonggang625401762@126．com
王树林：通讯作者，男，1951年生，教授，博士生导师，从事纳米材料制备及应用研究E-mail：usst516@163．com