针对灰铸铁激光熔覆的白口组织和开裂问题,研究了NiCuFeBSi合金材料及基体预热工艺对白口组织控制的影响,评价了合金力学性能。结果表明,NiCuFeBSi合金熔覆层界面白口组织宽度较小,基体预热温度升高时,白口组织呈现分散、断续状分布。半熔化区由于白口组织存在,显微硬度在此区达到峰值,向界面两侧呈递减趋势;NiCuFeBSi合金抗拉强度较高,横向抗拉强度大于纵向,其与HT250的对接试样抗拉强度受热影响区强度下降影响,强度小于NiCuFeBSi合金和HT250。熔覆层拉伸断裂机制为解理断裂为主、解理与准解理混合型断裂。
Due to existence of chill microstructure and cracks, influence of flaw control with laser cladding NiCuFeBSi alloy and preheating are investigated. Mechanical property of alloy is estimated as well. Results show that chill microstructure width of NiCuFeBSi alloy is extremely low. With preheating temperature increasing, the chill microstructure become discontinuous. Because of the generation of chill microstructure in semi-molten zone, microhardness in this zone is highest while descending at two sides of interface. Tensile strength of alloy is higher than HT250, furthermore, tensile strength along cross direction is higher than longitudinal direction. However, tensile strength of butt samples is lowest because of heat affection. Failure type of claddings is mainly cleavage fracture mixing quasi-cleavage fracture.
出处
《中国激光》
EI
CAS
CSCD
北大核心
2012年第12期67-73,共7页
Chinese Journal of Lasers
基金
国家973计划(2011CB013403)
国家自然科学基金(50975287)
"十二五"预研(51327040401)资助课题
关键词
激光技术
激光熔覆
灰铸铁
白口组织
预热温度
laser technique
laser cladding
gray cast iron
chill microstructure
preheating temperature
作者简介
董世运（1973-），男，研究员，主要从事激光熔覆再制造及其质量控制等方面的研究。E-mail：syd422@sohu．com.