摘要
以甲基丙烯酸缩水甘油酯(GMA)修饰聚六亚甲基胍盐酸盐(PHMG),制备端基具有甲基丙烯酸酯基的抗菌改性剂PHMG-GMA。将PHMG-GMA与树脂双酚A-甲基丙烯酸缩水甘油酯(Bis-GMA)、稀释剂二甲基丙烯酸二缩三乙二醇酯(TEGDMA)、填料纳米SiO2、光引发剂樟脑醌(CQ)混合均匀,经紫外灯固化后得到了具有抗菌性能的复合牙科材料。测试了该材料的抗菌性能,研究了SiO2、PHMG-GMA的加入对紫外透过率的影响。结果表明:随着SiO2含量的增加,材料的紫外透过率下降。当PHMG-GMA的质量分数为1.0%时,复合牙科材料对变形链球菌的抑菌率达到99.99%。
Polyhexamethylene guanidine（PHMG） with reactive methacrylate group,named as PHMG-GMA,was prepared by the reaction between polyhexamethylene guanidine（PHMG） and glycidyl methacrylate（GMA）.After homogeneously blending of nano-SiO2,PHMG-GMA,bisphenol A-bisglycidyl methacrylate（Bis-GMA）,triethylene glycol dimethacrylate（TEGDMA）,and camphorquinone（CQ）,and curing under UV lamp,an antibacterial dental composite was prepared.The antimicrobial rate and the effect of SiO2 and PHMG-GMA on the UV transmission were determined.Results showed that with the increasing of SiO2 content,UV transmission of the composite decreased.When w（PHMG-GMA） was 1.0%,the growth inhibition of this material against Streptococcus mutans reached 99.99%.
出处
《功能高分子学报》
CAS
CSCD
北大核心
2012年第3期248-253,共6页
Journal of Functional Polymers
基金
国家自然科学基金项目(50573020)
教育部留学归国人员科研启动基金资助项目
作者简介
作者简介：朱琳琳（1987-），女，上海人，硕士生，研究方向为抗菌材料。E-mail：linlin198708@yahoo．cn
通讯联系人：郑安呐，E-mail：zall@ecust．edu．cn