摘要
采用空气加压渗流技术制备了含宏观孔的开孔泡沫铝材料,通过多功能内耗仪采用内耗技术测试了泡沫铝在不同温度、不同频率和不同振幅下的内耗谱特征,研究表明与致密工业纯铝的阻尼能力相比,泡沫铝的阻尼能力得到很大的提高,泡沫铝的内耗随着测量频率的增加而增大,同时,内耗也随着应变振幅的增加而增大。经透射电子显微镜观察发现在晶界附近存在大量的位错亚结构。根据内耗测量和微观观察提出了泡沫铝中可能的阻尼机制:孔周围的应力集中和模式转换,孔洞/金属基体界面处由于动力学模量相差很大而使机械能转化为热能,孔洞发生不均匀的膨胀或畸变使外加应变能耗散为热能。
Experiments have been carried out to study the effects of macroscopic open-pores on the damping be havior of foamed commercially pure aluminum （FA）. The damping characterization was conducted on a multifunclion internal friction apparatus （MFIFA）. The FA specimens were prepared by air pressure infiltration process. The inter nal friction （IF） of the FA specimen was measured at different temperatures, different frequencies, and different am plitude dependences. The measured IF shows that FA has a damping capacity which is enhanced in comparison with bulk commercially pure aluminum, increases with increasing porosity, increases with decreasing macroporc size. increases with increasing frequency and increases with increasing strain amplitude. Transmission electron microscopy （TEM） observations show that moderate density of dislocation substructures exist near the grain boundaries in Ibe FA. In light of IF measurements and microstructural observations, the possible operative damping mechanisms FA are the stress concentration and mode conversion around macroscopic pores, the elastic modulus difference between the matrix and the macroscopic pores that results in a marked inhomogeneous stress, inhomogeneous expansi formation around acroscopic pores.
出处
《材料导报》
EI
CAS
CSCD
北大核心
2012年第12期122-124,132,共4页
Materials Reports
基金
江西省自然科学(青年)基金(0550050)
江西省教育厅科研项目(13-3-B-04)
关键词
宏观孔
泡沫铝
阻尼
内耗
macroscopic pores, foamed aluminum, damping, internal friction
作者简介
魏健宁：男，1973年生，教授，博士，硕士生导师，主要从事材料阻尼机理的研究Tel：0792-8334061）Email：cl_weiiianning@jju.edu．cn