摘要
采用等温溶解平衡法研究Na2B4O7-NaBr-Na2SO4-H2O四元体系在348 K的相平衡关系,测定了平衡液相的溶解度和密度。根据实验数据绘制相应相图。该四元体系相图中有1个共饱点E,3条单变量曲线E1E,E2E,E3E,3个结晶区的平衡固相分别为:NaBr,Na2SO4和Na2B4O7·5H2O。研究结果表明:该四元体系无复盐和固溶体生成,属于简单四元体系,NaBr对Na2B4O7·5H2O和Na2SO4有较强的盐析作用。并对NaBr和Na2B4O7在不同温度下含有的结晶水数进行了对比分析,简要讨论了密度变化规律。
The solubilities and densities of solution in Na2B4O7-NaBr-Na2SO4-H2O quaternary system at 348 K were determined by isothermal equilibrium method.Based on the experimental data,the equilibrium phase diagram was plotted,which consists of one invariant E,three univariant curves（E1E,E2E and E3E）,and three crystallization fields corresponding to NaBr,Na2SO4 and Na2B4O7·5H2O.The experimental results indicate that the quaternary system is of simple eutectic type and no double salt and solid solution,and sodium bromide has the salting-out effect on Na2B4O7·5H2O and Na2SO4.The densities transformation rules were discussed.
出处
《化学工程》
CAS
CSCD
北大核心
2012年第4期27-30,共4页
Chemical Engineering(China)
基金
国家自然科学基金资助项目(40973047)
四川省杰出青年学科带头人培养资助计划资助项目(08ZQ026-017)
教育部新世纪优秀人才资助计划资助项目(NCET-07-0125)
关键词
水盐体系
相平衡
硼酸盐
salt-water system
phase equilibrium
borate
作者简介
宁慧逸（1986-），女，硕士研究生，研究方向为化学工艺，E-mail：nhy．happy@163．com；
桑世华（1971-），女。博士，教授，通信联系人，研究方向为相平衡与相图及化学工艺，E-mail：sangsh@cdut．edu．cn。