摘要
以铝合金AA6061-T6和双相钢DP590为研究对象,通过正交试验方法研究了铆钉长度、凹模中部直径和凹模凸台高度对铝合金-高强钢自冲铆接接头成形规律、接头几何特征量、拉剪强度以及失效模式的影响规律,分析了影响自冲铆接接头强度的关键因素以及在2mm AA6061-T6+1.2mm DP590组合下的最优工艺参数组合,可为自冲铆接工艺优化提供有益的借鉴。
The self-piercing riveting of aluminum alloy AA6061-T6 and dual-phase high strength steel DP590 was studied. The design of orthogonal experiment （DOE） method was used to investigate the impact of the rivet length, the middle diameter and boss height of the die on the joint formation, geometry characteristics, tensile strength and failure modes. The key factors to affect self piercing riveted joint strength were researched. The optimal process parameters for the given material combination was analyzed. This study can ofter useful references for the process optimization of self piercing riveting.
出处
《汽车工程学报》
2011年第3期185-191,共7页
Chinese Journal of Automotive Engineering
基金
机械系统与振动国家重点实验室项目(MSV201109)
科技部国际科技合作计划资助课题(2010DFA72760)
上海市重点学科建设项目(ZXDF156)
关键词
铝钢异种连接
自冲铆接
汽车轻量化
正交试验设计
dissimilar materails
self-piercing riveting （SPR）
autobody lightweightening
design oforthogonal experiment （DOE）
作者简介
责任作者：金鑫（1986-），男，湖北宜昌人.海交通大学机械与动力工程学院硕士研究生，主要从事自冲铆接工艺研究。
通讯作者：李永兵（1975-），男，陕西扶风人。副教授，博士，2006年赴美国密西根大学研修，主要从事轿车车身先进焊接与连接工艺研究。Tel：021-34206288 E-mail：yongbinglee@sjtu．edu．cn