针对常规金属表面强化方法,对具有复杂形状或一些大尺寸零件的表面层强化比较困难这一现实情况出发,笔者提出了利用电液压脉冲水气射流,实现金属表面层强化这一新型方法。通过对金属表面强化前后的表面硬度、残余应力和金相组织观察的实验对比,得出了该方法可以大大提高金属表面层硬化程度、产生较大残余压应力和硬化层明显的实验结果。该实验成果为其今后在工程实践中推广应用提供了一定的借鉴依据。
There are more difficult to strengthen the surface of the metal which has the complex and large part by normal strengthen way, aiming at it, it put forward a new metal surface strengthening way which is to treat the surface of metal by electro hydraulic impulse water-air jet. The contrast experiment of the surface harhness, residual stres and metallographic structure of metal surface before and after strengthening shows that it can improve the hardness, residual stress and the hardening depth. The experimental results can provide some value in engineering practical application.
出处
《表面技术》
EI
CAS
CSCD
北大核心
2011年第4期19-22,共4页
Surface Technology
基金
科技部国际科技合作项目(2008DFA70300)
关键词
电液压脉冲
水气射流
硬化
残余应力
electro-hydraulic impulse
wate-air jet
hardening
residual stress
作者简介
裴江红（1973-），男，重庆人，博士，主要从事水射流强化金属表面、机械设计及理论的教学和研究。